Gas Shielded Arc Welding Wire
Introduction
Gas Shielded Arc Welding Wire
The gas shielded welding wire produced by our company is suitable for all position welding. It can adapt to a large welding current range. It has many advantages, stable arc during welding, less splas, beautiful weld forming, and high deposition efficiency, strong resistance to base material surface oxide, oil, and low porosity sensitivity of weld metal. Compared withsimilar products produced by other manufacturers, the welding wire products produced by our company are at an advanced level in terms of appearance quality, service performance, welding mechanical performance and other aspects.
The products are widely used in the welding of steel structures such as coal mining machinery, engineering machinery, ships, bridges, pressure vessels and construction, as well as the welding of other 50ompa carbon steel and low alloy steel, as well as the high-speed welding of thin plates and pipeline steel.
No.
Trade Name
Standard/Grad
Chemical composition
Deposited metal mechanical performance
Package
C
Mn
Si
P
S
Ni
Cr
Cu
Mo
Ti
V
AI
Zr
Tensile strengthRm(Mpa)
Yield strength Rp0.2(Mpa)
Elongatio percent(%)
Average impact strength(J)
gas
1
ER49-1
GB /T8110
AWSA5.18ER70S-7
0.09
1.89
0.78
0.016
0.013
0.017
0.008
0.16
542
423
29
Temperature
CO2
5kg,
15kg
20kg
2
ER50-2
GB /T8110
AWSA5.18ER70S-2
0.05
1.21
0.62
0.010
0.013
0.06
0.03
0.16
0.02
0.08
0.007
0.007
0.08
572
465
27
89(-30℃)
CO2
3
ER50-3
GB /T8110
AWSA5.18ER70S-3
0.09
1.05
0.65
0.014
0.013
0.02
0.017
0.17
0.004
0.003
542
423
29
116(-20℃)
CO2
4
ER50-6
GB /T8110
AWSA5.18ER70S-6
0.08
1.51
0.89
0.015
0.013
0.016
0.021
0.18
0.006
0.003
545
452
29
91(-30℃)
CO2
Video
Gallery
Introduction
Gas Shielded Arc Welding Wire
The gas shielded welding wire produced by our company is suitable for all position welding. It can adapt to a large welding current range. It has many advantages, stable arc during welding, less splas, beautiful weld forming, and high deposition efficiency, strong resistance to base material surface oxide, oil, and low porosity sensitivity of weld metal. Compared withsimilar products produced by other manufacturers, the welding wire products produced by our company are at an advanced level in terms of appearance quality, service performance, welding mechanical performance and other aspects.
The products are widely used in the welding of steel structures such as coal mining machinery, engineering machinery, ships, bridges, pressure vessels and construction, as well as the welding of other 50ompa carbon steel and low alloy steel, as well as the high-speed welding of thin plates and pipeline steel.
| No. | Trade Name | Standard/Grad | Chemical composition | Deposited metal mechanical performance | Package | ||||||||||||||||
| C | Mn | Si | P | S | Ni | Cr | Cu | Mo | Ti | V | AI | Zr | Tensile strengthRm(Mpa) | Yield strength Rp0.2(Mpa) | Elongatio percent(%) | Average impact strength(J) | gas | ||||
| 1 | ER49-1 | GB /T8110
AWSA5.18ER70S-7 |
0.09 | 1.89 | 0.78 | 0.016 | 0.013 | 0.017 | 0.008 | 0.16 | 542 | 423 | 29 | Temperature | CO2 | 5kg,
15kg 20kg |
|||||
| 2 | ER50-2 | GB /T8110
AWSA5.18ER70S-2 |
0.05 | 1.21 | 0.62 | 0.010 | 0.013 | 0.06 | 0.03 | 0.16 | 0.02 | 0.08 | 0.007 | 0.007 | 0.08 | 572 | 465 | 27 | 89(-30℃) | CO2 | |
| 3 | ER50-3 | GB /T8110
AWSA5.18ER70S-3 |
0.09 | 1.05 | 0.65 | 0.014 | 0.013 | 0.02 | 0.017 | 0.17 | 0.004 | 0.003 | 542 | 423 | 29 | 116(-20℃) | CO2 | ||||
| 4 | ER50-6 | GB /T8110
AWSA5.18ER70S-6 |
0.08 | 1.51 | 0.89 | 0.015 | 0.013 | 0.016 | 0.021 | 0.18 | 0.006 | 0.003 | 545 | 452 | 29 | 91(-30℃) | CO2 | ||||